Collected Item: “Development of a new system of solid ionic conductors based on multi-doped ceria for application in IT-SOFCs”
Врста публикације
Рад у часопису
Верзија рада
објављена верзија
Језик рада
енглески
Аутор/и (Милан Марковић, Никола Николић)
Marija Stojmenovic, Neda Nisic, Milan Zunic, Francesco Basoli, Jelena Gulicovki, Ivica Ristovic, Milan Kragovic
Наслов рада (Наслов - поднаслов)
Development of a new system of solid ionic conductors based on multi-doped ceria for application in IT-SOFCs
Наслов часописа
Processing and Application of Ceramics
Издавач (Београд : Просвета)
National Library of Serbia
Година издавања
2022
Сажетак на српском језику
Nanodimenzionisana multi-dopirana cerija sa sastavom Ce0.8Nd0.0025Sm0.0025Gd0.005Di0.095I0.095O2-d (CNSDI) kao perspektivni čvrsti jonski provodnik je dobijen modifikovanim glicin-nitratnim postupkom (MGNP) i samopropagirajućom reakcijom na sobnoj temperaturi (SPRT). Presovani peleti oba praha su sinterovani na 1550 °C za 2 h u vazdušnoj atmosferi. Dobijeni sinterovani uzorci su okarakterisani KSRPD, Raman spektroskopijom, FESEM, EDS i EIS metode. Uprkos visokoj temperaturi sinterovanja, KSRPD i FESEM analize uzorci su potvrdili odgovarajuće dimenzije zrna sa strukturom fluorita. Ukupna koncentracija uvedenih dodataka (k = 0,2) u strukturi CeO2 nakon što je proces sinterovanja potvrđen EDS analizom.
Nakon sinterovanja, Ramanova spektroskopija je potvrdila zadržavanje slobodnih mesta kiseonika u rešetki cerije, što je u skladu sa poboljšanjem jonske provodljivosti čvrstih jonskih provodnika. Najveća vrednost ukupne provodljivost je dobijena za sinterovani uzorak MGNP na 700 °C (4,22 × 10−2 S cm−1.), sa odgovarajućom energijom aktivacije od 0,26 eV.
Nakon sinterovanja, Ramanova spektroskopija je potvrdila zadržavanje slobodnih mesta kiseonika u rešetki cerije, što je u skladu sa poboljšanjem jonske provodljivosti čvrstih jonskih provodnika. Najveća vrednost ukupne provodljivost je dobijena za sinterovani uzorak MGNP na 700 °C (4,22 × 10−2 S cm−1.), sa odgovarajućom energijom aktivacije od 0,26 eV.
Сажетак на енглеском језику
Nanosized multi-doped ceria with composition Ce0.8Nd0.0025Sm0.0025Gd0.005Dy0.095Y0.095O2-δ (CNSGDY) as perspective solid ionic conductor was obtained by modified glycine-nitrate procedure (MGNP) and room temperature self-propagating reaction (SPRT). The pressed pellets of both powders were sintered at 1550 °C for 2 h in an air atmosphere. The obtained sintered samples were characterized by XRPD, Raman spectroscopy, FESEM, EDS and EIS methods. Despite a high temperature of sintering, XRPD and FESEM analyses of the samples confirmed appropriate dimensions of grains with fluorite structure. Overall concentration of introduced dopants (x = 0.2) in the structure of CeO2 after the sintering process was confirmed by EDS analysis. After sintering, Raman spectroscopy confirmed retention of the oxygen vacancies in the ceria lattice, which is in accordance with the improvement of ionic conductivity of solid ionic conductors. The highest value of total conductivity was obtained for the sintered MGNP sample at 700 °C (4.22 × 10−2 S cm−1 ), with the corresponding activation energy of 0.26 eV.
Волумен/том или годиште часописа
16
Број часописа
4
Почетна страна
391
Завршна страна
401
DOI број
10.2298/PAC2204391S
ISSN број часописа
1820-6131
Географско подручје на које се односи публикација
-
Кључне речи на српском (одвојене знаком ", ")
"CeO2" "sinterovanje" "električna provodljivost" "impedansna spektroskopija" "gorive ćelije"
Кључне речи на енглеском (одвојене знаком ", ")
"CeO2" "sintering" "electrical conductivity" "impedance spectroscopy" "fuel cells"
Линк
http://dx.doi.org/10.2298/PAC2204391S
Шира категорија рада према правилнику МПНТ
M20
Ужа категорија рада према правилнику МПНТ
М23
Пројект у склопу кога је настао рад
Ministry of Education, Science and Technological Development of the Republic of Ser- bia [451-03-495 68/2022-14/200017, 1702203, 1702205]
Степен доступности
Отворени приступ
Лиценца
Creative Commons – Attribution-Share Alike 4.0 International
Формат дигиталног објекта
.pdf